The common question of high-strength bolts
1. What materials is the high-strength bolts?
High-strength bolt generally refers to the bolt of the grade exceeded 10.9s. It should adopt the meterial of 34CrNiMo or 34CrNi3Mo. Heatting treatment is indispensable.

2. Why steel bolt is forbidden from the rain before the final twisted ?
In case of rust!

3. Can bolt be used in aluminum-connection ? 
Do you want to use aluminum to withstand heavy loads? Different strength-grades of material can not be equipped to use. if it has to use, the preload bolts can not exceed the ultimate strength aluminum could be able to bear.
4. What are the requirements to the construction pretension of high strength bolt?
It should be fitted the design requirements. Lack of tighten-value or over tighten-value should not exceed 10% of regulation. The designning pre-tension value of various types of bolts are the following table:
Bolt material Diameter (mm) Design pre-tension (KN)
20MnTiB40B M22 200
M24 230
Steel 45# M22 160 
5. The problems of high-strength fasteners? 

Guarantee strength requirements. Wedge load and load to ensure the product is to be assessed under tensile loading the mechanical properties of key projects (A Class), is particularly important for high-strength fasteners. Assessment to ensure load is tension in the load bearing requirements of resistance to plastic deformation of products, if the index below standard, as tightening force and work load, which may be plastic deformation, thereby reducing the preload to loose connection . Fatigue test is assessing the tensile strength of bolts and head pole with strength. 
Hardness requirements. Mechanical properties of fasteners hardness evaluation is an important indicator of performance for all grades of material used is different, when the mechanical fasteners used performance levels is an important basis for the installation and use of performance levels established in accordance with the work load and install torque, for a particular material, hardness should be controlled at a reasonable level, high hardness may reduce the fatigue resistance of the product, some enterprises to improve product strength, hardness control at a higher level, resulting in some of the products exceeded. 
Excessive decarburization layer. Decarburization is also a Class A project, due to decarburization, making parts greatly reduced the surface hardness and strength of surface contact fasteners serious impact strength and fatigue life in particular parts of thread damage is more prominent. The main reason is caused by decarbonization decarbonization of raw materials, materials and products restructuring process of decarburization decarburization during heat treatment. 
Copyright ?Beijing Jinzhaobo high-strength fasteners Co., Ltd
Contact: 86-10-60553140 60553141 mobile: 18710178966 contact name: Mr.Dong
Address: NO.46-12, South Street of Beiyuan, Tongzhou District, Beijing City.